Sikadur®-42 HP
DEEP POUR PRE-PROPORTIONED, PRECISION EPOXY GROUTING SYSTEM
Sikadur®-42 HP, is a high strength, multi purpose, three-component, low exotherm, low dusting, solvent-free, moisture-insensitive, epoxy grouting system designed to seat and support high demand equipment.
- Low peak exotherm.
- Low dusting, ready-to-mix, pre-proportioned kits.
- Moisture insensitive.
- Corrosion and impact resistant.
- Stress and chemical resistant.
- High compressive, tensile and shear strengths.
- High vibration resistance.
- Low coefficient of thermal expansion, compatible with concrete.
- Material does not require heated transportation.
Usage
Sikadur®-42 HP may only be used by experiencedprofessionals.
- Precision seating of baseplates
- Grouting under equipment, including heavy impact and vibratory machinery, reciprocating engines, compressors, pumps, presses, etc.
- Grouting under crane rails
Advantages
- Low peak exotherm.
- Low dusting, ready-to-mix, pre-proportioned kits.
- Moisture insensitive.
- Corrosion and impact resistant.
- Stress and chemical resistant.
- High compressive, tensile and shear strengths.
- High vibration resistance.
- Low coefficient of thermal expansion, compatible with concrete.
- Material does not require heated transportation.
Packaging
36 kg - 3 component kit consisting of:
472516 Sikadur 42 HP Part A - Resin 5 kg
472519 Sikadur 42 HP Part B - Hardener 1 kg
731898 Sikadur 42 HP Part C 15 kg bag (2 x 15 kg Bags per kit)
Colour
Concrete Grey
Product Details
Shelf life
24 months from date of production
Storage conditions
Stored properly in original and unopened, sealed and undamaged packaging, in dry conditions at temperatures between +5°C and +30°C. Protect from direct sun light.
Density
2,130 kg/m3 (A+B+C)
Effective bearing area
> 90% | (ASTM C 1339) |
Compressive strength
6 hrs | ~ 20 MPa |
1 day | ~ 90 MPa |
7 days | ~ 100 MPa |
Test specimen cured and tested at +23oC and 50 mm cube size.
Modulus of elasticity in compression
~ 18,000 MPa | (ASTM D 695-96) |
Tensile strength in flexure
> 35 MPa | (ASTM C 580) |
Modulus of elasticity in flexure
~ 16,000 MPa | (EN 53452) |
Tensile strength
> 14 MPa | (ASTM D 638) |
Tensile adhesion strength
~ 9 MPa (on steel) > 3.5 MPa (concrete failure) | (ISO 4624, EN 1542 and EN 12188) |
Shear adhesion strength
> 47 MPa (concrete failure) | (ASTM C 882) |
Creep
4.14 N/mm2 / 31’500 N (+60°C) 1.10% 2.76 N/mm2 / 21’000 N (+60°C) 0.21% API requirements: 0.5% with 2.76 N/mm2 load | (ASTM C 1181) |
Shrinkage
Linear Shrinkage: -0.027% Linear Shrinkage: -0.03% | (ASTM C 531) (EN 52450) |
Coefficient of thermal expansion
2.1 x 10-5 mm/mm/°C (Temp. range -30°C to +30°C) 4.4 x 10-5 mm/mm/°C (Temp. range +24°C to +100°C) | (ASTM C 531) |
Thermal compatibility
No delamination / pass | (ASTM C 884) |
Water absorption
0.059% (7 days) | (ASTM C 413) |
Application
Mixing ratio
Part A : B : C = 1.67 : 0.33 : 10 by weight (Standard)
Solid / liquid = 5 : 1 by weight
Possibility to adjust the Mixing ratio, depending on Flowability:
Part A : B : C = 1.67 : 0.33 : (9-12) by weight
Solid / liquid = (4.5 – 6) : 1 by weight
Layer thickness
Minimum grout depth: 10 mm
Maximum grout depth: 150 mm
Temperature | Layer thickness maximum |
10 oC - 20 oC | 150 mm |
20 oC - 30 oC | 120 mm |
Peak exotherm
44°C (at +23°C) | (ASTM D 2471) |
Material temperature
Sikadur®-42 HP must be applied at temperatures between +10°C and +30°C.
Condition the material by also storing at this temperature for 48 hours before use.
Ambient air temperature
+10°C min. / +30°C max.
Substrate temperature
+10°C min. / +30°C max.
Substrate moisture content
≤ 4% pbw
Pot Life
(200g, adiabatic testing)
5 : 1 : 30 | 130 mins at +10 oC | 75-80 mins at +23 oC |
The potlife begins when the resin and hardener are mixed. It is shorter at high temperatures and longer at low temperatures. The greater the quantity mixed, the shorter the potlife. To obtain longer workability at high temperatures, the mixed adhesive may be divided into portions. Another method is to chill parts A+B and C before mixing them (i.e. only when application temperatures are above +20°C).
Yield
36 kg kit yields approximately 16.9 litres of grout
SUBSTRATE QUALITY
Mortar and concrete must be older than 28 days (dependent on minimum strength requirements).
Verify the substrate strength (concrete, natural stone etc.).
The substrate surface (all types) must be clean, dry and free from contaminants such as dirt, oil, grease, existing surface treatments and coatings etc.
Steel substrates must be de-rusted to a standard equivalent to Sa 2.5.
The substrate must be sound and all loose particles must be removed.
Substrate must be dry or mat damp and free from any standing water, ice etc.
SUBSTRATE PREPARATION
Surface and base plate contact area must be clean and sound. For best results, the substrate should be dry. Remove dust, laitance, oils, grease, curing compounds, impregnations, waxes, foreign particles, coatings, and disintegrated materials by mechanical means, i.e. chipping with a chisel, blastcleaning etc. All anchor pockets or sleeves must be free of water. Blastcleaning metal base plates to an acceptable quality standard equivalent to SA 2.5 for maximum adhesion. Apply grout immediately to prevent re-oxidizing.
Forming:
The consistency of the Sikadur®-42 HP epoxy grout system requires the use of permanent or temporary forms to contain the material around base plates, for example. In order to prevent leakage or seepage, all of these formers must be sealed. Apply polyethylene film or wax to all forms to prevent adhesion of the grout. Prepare the formwork to maintain more than 100 mm liquid head to facilitate placement. A grout box equipped with an inclined trough attached to the form will enhance the grout flow and minimize air encapsulation.
MIXING
Pre-batched units:
Mix components A and B in the component A pail for 3 min with a paddle attached to a low speed drill (300-450 rpm). Avoid aeration while mixing until the material becomes uniformly blended in colour and viscosity. Place the mixed epoxy into an appropriate mixing vessel. Slowly add the contents of component C (to keep air entrapment at a minimum) dependent on flow requirements (observe the correct mixing ratio) and mix until uniform and homogeneous. (approx. 5 min)
Mix only that quantity which can be used within its potlife.
Bulk packing (not pre-batched):
First, stir each component thoroughly. Add the components in the correct proportions into a suitable mixing pail. Mix the components. Use an electric low speed mixer, etc as above for the pre-batched units.
Never mix Component A and B without adding component C (as the exothermic reaction between A and B alone generates excess heat)
Leave Sikadur®-42 HP to stand in the normal mixing vessel until the majority of entrained air bubbles have dispersed.
CLEANING OF EQUIPMENT
Sweep excess grout into appropriate containers for disposal before it has hardened. Dispose of in accordance with applicable local regulations. Uncured material can be removed with Sika Colma Cleaner. Cured material can only be removed mechanically.