SikaBond®-203 Universal Vinyl Adhesive
SikaBond®-203 Universal Vinyl Adhesive is a water-based, low VOC, high perfomance, multi purpose adhesive designed for various PVC and common backed textile floor coverings.
- Multi flooring types
- Low odour
- Low VOC
- Strong tack build
- Easy to trowel
- Final hard set cure
Usage
Dimensional stable PVC Flooring Linoleum Luxury Vinyl Tiles (LVT) Sanded back flooring up to 4mm Luxury Vinyl Plank (LVP) Textile floor coverings with all common backingAdvantages
- Multi flooring types
- Low odour
- Low VOC
- Strong tack build
- Easy to trowel
- Final hard set cure
Packaging
14kg pail
Colour
Cream
Product Details
Composition
1-component dispersion
Shelf life
SikaBond®-203 Universal Vinyl Adhesivehas a shelf life of 12 months from the date of production, if it is stored properly in undamaged, original, sealed packaging, and if the storage conditions are met.
Storage conditions
SikaBond®-203 Universal Vinyl Adhesiveshall be stored in dry conditions, protected from direct sunlight and at temperatures between +5 °C and +25 °C.
Density
~1.2kg/litre
Consistency
Thick paste
Application
Ambient air temperature
+15 °C to +35 °C
Substrate temperature
During laying and until SikaBond®-203 Universal Vinyl Adhesive has fully cured, the substrate and ambient temperatures shall be between +15 °C and +35 °C. Where underfloor heating units are installed, the heating units shall be turned on prior to laying the floor covering for a minimum of 7 days to ensure that the moisture condition of the heated subfloor will permit successful laying of the coverings. Heating units shall be turned off 48 hours prior to the commencement of installation. The heating units shall not be turned on again until 48 hours after the laying is completed.
Substrate moisture content
Moisture content requirement:
85% RH (in-situ probe method: ASTM F2170) or 15 g/m2 per 24 hrs (moisture vapour emission rate surface test ASTM F1869) prior to installation.
pH requirement:
The pH / alkalinity of the concrete must not be higher than 10.
Note: AS1884-2021 should be followed in conjunction with the guidelines of the soft floor manufacturer.
Curing time
~24 h (final strength after ~72 h)
Skin time / laying Time
~20-40 minutes
Flash-off time
~20-40 minutes
Consumption
Smooth backed domestic sheet vinyl | Trowel U1 | ~5m²/kg |
Smooth backed floor coverings | Trowel V1 | ~4m²/kg |
Texture backed floor coverings | Trowel V2 | ~2.5m²/kg |
APPLICATION INSTRUCTIONS
For the application of SikaBond®-203 Universal Vinyl Adhesive all standard construction guidelines and relevant valid data sheets apply.
SUBSTRATE PREPARATION
- The substrate must be clean, dry, sound, absorbent and homogeneous, free from oils, grease, dust and loose or friable particles. Paint, cement laitance, prior adhesives, floorcoverings and other poorly adhering contaminants must be removed.
- All surfaces must be prepared in accordance to the current Australian Standards AS1884:2021 - Floor coverings - Resilient floor and tiles - Installation practices.
- Prime absorbent substrate with Sikafloor® -01 Primer prior to application of SikaBond®-203 Universal Vinyl Adhesive.
- Defective subfloors shall be treated by taking appropriate measures e.g. grinding, milling, vacuuming, priming or self-levelling.
- Mastic asphalt and other non-absorbent subfloors as well as rubber floor coverings may require specific self-levelling compound layer thicknesses. For appropriate layer thicknesses refer to the relevant valid data sheets.
- Concrete and/or cement screeds must be ground and thoroughly cleaned with an industrial vacuum.
- When installing floor covering with underfloor heating, existing measuring points have to be checked regarding the moisture content of the subfloor.
CLEANING OF EQUIPMENT
Clean excess adhesive immediately using a lightly damp cloth. Clean tools immediately after use with warm soapy water. Dried adhesive may be softened using a Sika cleaner such as Sika® Colma Cleaner.
IMPORTANT: Do not use solvent cleaner directly on finish floorcovering, as the solvent cleaner can potentially cause damage to the surface.