Sikafloor®-305 W

VOC Emission certificate according to AgBB und DIBt approval requirements (AgBB – Committee for Health-related Evaluation of Building Products, DiBt – German Institute for Building Technology), Eurofins report No. 769855D

• Synthetic resin screed material according to EN 13813:2002, Declaration of Performance and provided with the CE marking.
• Coating for surface protection of concrete according to EN 1504-2:2004,  Declaration of Performance 0208010400500000031041, certified by notified factory production control certification body 0620, and provided with the CE marking.
• Fire classification acc. to EN 13501-1, Test reports 08-198, 08-199 and CR-13- 167/1, Ghent University

PUR

The product must be stored properly in original, unopened and undamaged sealed packaging, in dry conditions at temperatures between +5 °C and +30 °C.

All Density values at +23 °C

Resistant to many chemicals. Contact Sika technical service for specific information.

Part A : Part B = 85 : 15 (by weight)

+10 °C min. / +30 °C max.

75 % max.
During curing the relative humidity should not exceed 75 %. Adequate fresh air ventilation must be provided to remove the excess moisture from the curing product.

Beware of condensation!
The substrate and uncured floor must be at least 3 °C above dew point to reduce the risk of condensation or blooming on the floor finish.

+10 °C min. / +30 °C max.

Caution: End of potlife is not noticeable.

Before overcoating Sikafloor®-305 W allow:

Based on relative humidity of max. 70 % and good ventilation. Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.

Note: Times are approximate and will be affected by changing ambient conditions

~0,13–0,15 kg/m²/layer

This figure is theoretical and does not allow for any additional material due to surface porosity, surface profile, variations in level and wastage etc.

When used in high wear conditions, for example where rolling office chairs occur, a double layer Sikafloor®-305 W is highly advisable. A double layer is increasing the mechanical strength of the system and it resistance against office chairs particularly.

Prior to mixing, stir part A mechanically. When all of part B has been added to part A, mix continuously for 3 minutes until a uniform mix has been achieved. During the mixing of the Components A and B add 5–7 % of clean water. To ensure thorough mixing pour materials into another container and mix again to achieve a consistent mix. After mixing give the material a rest for 10 minutes. Over mixing must be avoided to minimise air entrainment.
Mixing Tools:
Sikafloor®-305 W must be thoroughly mixed using a low speed electric stirrer (300–400 rpm) or other suitable equipment.

Prior to application, confirm substrate moisture content, relative humidity and dew point. Uniformly spread Sikafloor®-305 W by using a short pile nylon roller. Sikafloor®-305 W can also be applied by using airless spray equipment. A seamless finish can be achieved if a “wet” edge is maintained during application.

Clean all tools and application equipment with water immediately after use. Hardened and/or cured material can only be removed mechanically.