Sikagard®-550 W Elastic
Sikagard®-550 W Elastic is a one component, plasto-elastic coating based on UV-curing acrylic dispersion with excellent crack-bridging properties even at temperatures below 0 °C.
Sikagard®-550 W Elastic complies with the requirements of EN 1504-2 as protective coating.
- Crack-bridging even at low temperatures (-20°C)
- High diffusion resistance against CO2 reducing the rate of carbonation
- Water vapour permeable
- Very good resistance against weathering and ageing
- Environmentally friendly (solvent free)
- Reduced tendency to dirt pick up and contamination
Usage
Sikagard®-550 W Elastic is used for protection and enhancement of concrete structures (normal and lightweight concrete), especially exposed outdoor concrete surfaces with a risk of cracking.Sikagard®-550 W Elastic is used with concrete repair works as an elastic protective coating on Sika® smoothing mortar (refer to relevant product / system data sheet), fibre cement and overcoating of existing soundly adhering coatings
- Suitable for protection against ingress (Principle 1, method 1.3 of EN 1504-9),
- Suitable for moisture control (Principle 2, method 2.3 of EN 1504-9)
- Suitable for increasing the resistivity (Principle 8, method 8.3 of EN 1504-9)
Advantages
- Crack-bridging even at low temperatures (-20°C)
- High diffusion resistance against CO2 reducing the rate of carbonation
- Water vapour permeable
- Very good resistance against weathering and ageing
- Environmentally friendly (solvent free)
- Reduced tendency to dirt pick up and contamination
Packaging
15 lt plastic pail
Colour
Thixotropic liquid available in almost every colour shade.
Product Details
APPROVALS / CERTIFICATES
EN 1504-2 performance testing, LPM Report A-33’882-2 dated July 09
The product is included in a compilation of tested products and systems as per
OS 5a (OS DII) at the German Institute of Road Systems
Determination of dynamic crack bridging properties according to EN 1062-7, report P8690a dated 27/08/2014, Kiwa Polymer Institut GmbH
Protective coating according to EN 1504-2, DoP 02 03 03 03 002 0 000003 1125; certified by Factory Production Control Body: 0921; certificate 0921-BPR-2046 and provided with the CE-mark
Composition
Acrylate dispersion
Shelf life
24 months from date of production if stored properly in undamaged and unopened original sealed packaging.
Storage conditions
Store in cool and dry conditions. Protect from direct sunlight and frost.
Density
~ 1.30 kg/l (at +20°C)
Solid content by mass
~ 65%
Solid content by volume
~ 53%
System structure
System | Product 1) | Number of applications |
Priming 2) | Sikagard®-552 W Aquaprimer | 1 |
Top coat 3) | Sikagard®-550 W Elastic | 2 – 3 |
Crack bridging ability
Class A1 (-20°C) - 2 coats | (EN 1062-7) |
Class B2 (-15°C) - 3 coats |
Dry Film Thickness | 310 µ |
Crack Width at Break | 1.5 mm |
Crack Bridging Ability | 5.0 |
Tensile adhesion strength
2.9 (2.8) N/mm² | (EN 1542) |
Capillary absorption
w = 0.02 kg/(m²h0.5) | (EN 1062-3) |
Permeability to water vapour
Dry Film Thickness | d = 210 µm |
Equivalent Air Layer Thickness | SD = 1.0 m |
Diffusion Resistance Coefficient | µ = 2,944 |
Permeability to carbon dioxide
Dry film thickness | d = 210 µm |
CO2 Diffusion Coefficient | D = 3.7 x 10-07 cm2/sec |
Diffusion Resistance Coefficient | µ = 5.4 x 105 |
Equivalent air layer thickness | R = 112 m |
Equivalent Thickness of Concrete | Sc = 28 cm |
Behaviour after artificial weathering
Pass after 2000 hours | (EN 1062-11) |
Freeze thaw de-icing salt resistance
2.9 (2.1) N/mm² | (EN 13687 part 1 & part 2) |
Application
Layer thickness
Minimum required dry film thickness to achieve the required characteristics (CO2 equivalent air thickness of 50 m) ≈ 160 μm.
Minimum required dry film thickness to achieve full durability characteristics (CO2 diffusion, adhesion after thermal cycling and crack bridging) ≈ 340 μm.
Ambient air temperature
+8°C min. / +35°C max.
Relative air humidity
< 80%
Dew point
Temperature must be at least 3°C above dew point.
Substrate temperature
+8°C min. / +35°C max.
Waiting time to overcoating
Waiting time between coats at +20°C substrate temperature:
Previous coating | Waiting time | Next coating |
Sikagard®-552 W Aquaprimer | 5 hours min. | Sikagard®-550 W Elastic |
Sikagard®-550 W Elastic | 8 hours min. | Sikagard®-550 W Elastic |
Applied product ready for use
Full cure: ~ 7 days at +20°C
Consumption
Product | Per coat |
Sikagard®-552 W Aquaprimer | ~ 0.10 - 0.15 kg/m2 |
Sikagard®-550 W Elastic | ~ 0.25 - 0.35 kg/m2 |
APPLICATION
Apply Sikagard®-552 W AquaPrimer evenly onto the substrate.
Sikagard®-550 W Elastic can be applied by brush, roller or airless spray.
For more details, refer to Protective Coating Application Method Statement.
CLEANING OF EQUIPMENT
Clean all tools and application equipment with clean water immediately after use.
Hardened / cured material can only be removed mechanically.
For Sikagard®-551 S Elastic Primer use Sika® Thinner C.