SikaForce®-712 L80

Long open time, low viscous 2-component adhesive for panel bonding

SikaForce®-712 L80 is a long open time, low viscous 2-component polyurethane adhesive for bonding sandwich panels and similar constructions of various materials.  

  • Low density
  • Low viscosity
  • Long open time
  • Room temperature curing
  • Solvent free
 
Product Data Sheet Show all documents

PRODUCT BENEFITS

  • Low density
  • Low viscosity
  • Long open time
  • Room temperature curing
  • Solvent free
 

Usage

SikaForce®-712 L80 is used primarily for bonding of metal, fiber cement, wood and glass fiber reinforced plastic to expanded and extruded polystyrene foam, polyurethane foam and mineral wool in the manufacturing of sandwich elements and other constructions. This product is suitable for experienced professional users only. Tests with actual substrates and conditions have to be performed, ensuring adhesion and material compatibility.  

Packaging

Component A (Resin): 25kg Pail

Component B (Hardener): 5kg Can & 250kg Drum

Product Details

Typical Product Data
Properties

Component A

SikaForce®-712 L80

Component B
SikaForce®-010

Chemical base

Polyols

Isocyanate derivatives

Colour (CQP001-1)

 

mixed

Beige

Brown

Beige

Cure mechanism

Polyaddition

Density (uncured)

 

mixed (calculated)

1.46 g/cm3

1.23 g/cm3

1.41 g/cm3

Solid content

100 %

100 %

Mixing ratio

by volume

by weight

100 : 30

100 : 26

Viscosity (CQP029-4)

Rheometer, PP25, shear rate 10 s-1, d=1 mm

mixed

7 000 mPa∙s A

300 mPa∙s A

4 000 mPa∙s A

Application temperature

15 – 30 °C

Pot-life (CQP536-3)

85 minutes A

Open time (CQP526-3)

155 minutes A

Press time (CQP590-4)

1 MPa

205 minutes A

Shore D hardness (CQP023-1 / ISO 48-4)

70 B

Tensile strength (CQP543-1 / ISO 527)

14 MPa B

Elongation at break (CQP543-1 / ISO 527)

55 % B

Tensile lap-shear strength (CQP546-1 / ISO 4587)

10 MPa B

Shelf life

12 months

9 months

CQP = Corporate Quality Procedure

A) 23 °C / 50 % r.h.

B) 12 weeks at 23 °C / 50 % r.h.
Technical Information

CURE MECHANISM

The curing of SikaForce®-712 L80 takes place by a chemical reaction of the two components. Higher temperatures speed up the curing process and lower slow it down.

CHEMICAL RESISTANCE

In case of chemical or thermal exposure, conduct project related testing.

Application

Application Information

Surface preparation

Surfaces must be clean, dry and free from grease, oil, dust and contaminants. After the cleaning process, a physical or chemical pre-treatment might be required, depending on surface and type of material. The type of pre-treatment must be determined by tests.

Application

Typically a coat weight between 150 and 350 g/m2 is applied, depending on the substrates to be bonded. The specific coat weight for a given substrate combination must be determined by tests.

The procedure for manual application is as follows: Ensure that the A-component is stirred thoroughly to avoid any sediment or separation, taking care not to stir too vigorously as this may introduce air into the product. Add the B-component in the specified ratio and stir thoroughly, ensuring a homogeneous mixture is achieved.

Apply before reaching half of the pot-life and join parts together within the open time. Consider that, if mixed in larger amounts, the exothermic reaction can reduce the pot-life and open time significantly.
For automated applications, contact the System Engineering Department of Sika Industry.

 

Pressing

An adequate bonding pressure is necessary to obtain a voidless contact between the substrates and the adhesive. The specific pressure is, however, dependent on the core material and must be determined by tests. The pressure must always be below the maximum compressive strength of the core. After starting the press process, do not release the pressure until the press time has elapsed.

Removal

Uncured SikaForce®-712 L80 may be removed from tools and equipment with SikaForce®-096 Cleaner. Once cured, the material can only be removed mechanically.
Hands and exposed skin have to be washed immediately using hand wipes such as Sika® Cleaner-350H or a suitable industrial hand cleaner and water.

Do not use solvents on skin.

STORAGE CONDITIONS

SikaForce®-712 L80 has to be kept between 10 °C and 30 °C in a dry place. Do not expose it to direct sunlight or frost. After opening of the packaging, the content has to be protected against humidity.
The lowest allowed temperature during transportation is -20 °C for max. 7 days.