Product Data Sheet Show all documents

Sikafloor® Marine-504

Water-based, 2-component, polyurethane, clear, matt topcoat for internal decks

Sikafloor® Marine-504 is a water-based, 2-component, polyurethane, clear, matt topcoat for internal decks. It is used as a component of the Sikafloor® Marine Deco systems. Sikafloor® Marine-504 has been tested in accordance with the FTP Code system and approved in accordance with IMO Marine Equipment Directives.  

  • Excellent working characteristics
  • Very low VOC emission
  • IMO approved
  • Easy to clean
 
Sikafloor® Marine-504
Product Data Sheet Show all documents

PRODUCT BENEFITS

  • Excellent working characteristics
  • Very low VOC emission
  • IMO approved
  • Easy to clean
 

Usage

Sikafloor® Marine-504 is designed as a component of the Sikafloor® Marine Deco systems for internal decks in ship and boat construction. This product is suitable for experienced professional users only. Tests with actual substrates and conditions have to be performed to ensure adhesion and material compatibility.  

Packaging

Sikafloor® Marine-504 (A)

Pail

6 kg

Sikafloor® Marine-504 (B)

Pail

1.5 kg

 

Product Details

Typical Product Data
Properties

Sikafloor® Marine-504 (A)

Sikafloor® Marine-504 (B)

Chemical base

Acrylic dispersion

Isocyanate

Colour (CQP001-1)

White

Transparent

Density

 

mixed (+ 5 % H2O)

1.1 kg/l

1.1 kg/l

1.1 kg/l

Solid content

57 %

Mixing ratio

by weight (A:B)

80 : 20

Application temperature

substrate / climate

10 ─ 30 °C A, B

Pot-life

at 10 °C

at 20 °C

at 30 °C

50 minutes

30 minutes

20 minutes

Shelf life

6 months C

12 months C

CQP = Corporate Quality Procedure

A) Substrate must be 3 °C above dew point

B) Maximum 80 % r. h.C) stored in sealed container in up-right position in a dry place between 5 and 30 °C, protected from direct sunlight
Technical Information

CURE MECHANISM

The curing of Sikafloor® Marine-504 takes place by a chemical reaction of the two components.
Higher temperatures speed up and lower temperatures slow down the curing process.

CHEMICAL RESISTANCE

For advice on chemical resistance contact the Technical Department of Sika Industry.

Application

Application Information

Surface preparation

Dust, loose and friable material must be completely removed from all surfaces before application of the product, preferably by brush or vacuum. Ensure that substrates are clean, dry and free from all contaminants such as dirt, oil, grease, coatings and other surface treatments.

Application

Prior to application confirm relative air humidity and dew point.

When starting to coat, make sure the coating rollers are well saturated with product.

After proper mixing the product is poured and spread out on the floor in respect of the coat weight. Note: Keep an eye on the pot life since the end of the pot-life is not visible.

Roll with a larger 50 cm roller in one direction cross the working direction to eliminate lap-marks.

Always consult the most current corresponding Application Manual.

 

Curing

Indications regarding curing details see table below.

Tempera-
ture

Foot traffic

Light traffic

Full cure

10 °C

36 hours

48 hours

6 days

20 °C

16 hours

24 hours

4 days

30 °C

12 hours

18 hours

3 days

Removal

Uncured Sikafloor® Marine-504 can be removed from tools and equipment with water. Once cured, the material can only be removed mechanically.
Hands and exposed skin have to be washed immediately using hand wipes such as Sika® Cleaner-350H or a suitable industrial hand cleaner and water.

Do not use solvents on skin.

Application limits

Freshly applied Sikafloor® Marine-504 must be protected from damp, condensation and water for at least 5 days. Uncured material reacts in contact with water (foaming).