Product Data Sheet Show all documents

Sikaplan® WP 1100-30 HL

SHEET WATERPROOFING MEMBRANE for BASEMENTs AND TUNNELs

Sikaplan® WP 1100-30 HL is a flexible, homogeneous sheet waterproofing membrane with a signal layer, based on premium-quality polyvinylchloride (PVC-P).

  • High resistance to ageing
  • Based on virgin material with consistent quality
  • Without DEHP (DOP) plasticisers
  • With signal layer to indicate damages
  • Optimized flexibility, tensile strength and multi-axial elongation
  • Elastic material behaviour
  • High resistance to mechanical influences
  • Flexible in cold temperatures
  • Suitable for contact with acidic soft water and alkaline environments
  • Resistant to root penetration and micro-organisms
  • Optimized workability, thermal weldable
  • Can be installed on damp and wet substrates
  • Temporary UV stability for installation
  • Self-extinguishing in fire
 
Product Data Sheet Show all documents

Usage

Waterproofing of tunnels and basements against water ingress

Advantages

  • High resistance to ageing
  • Based on virgin material with consistent quality
  • Without DEHP (DOP) plasticisers
  • With signal layer to indicate damages
  • Optimized flexibility, tensile strength and multi-axial elongation
  • Elastic material behaviour
  • High resistance to mechanical influences
  • Flexible in cold temperatures
  • Suitable for contact with acidic soft water and alkaline environments
  • Resistant to root penetration and micro-organisms
  • Optimized workability, thermal weldable
  • Can be installed on damp and wet substrates
  • Temporary UV stability for installation
  • Self-extinguishing in fire
 

Packaging

Roll size

2.20 m (width) × roll length individual as specified

Colour

Surface

smooth

Colour

signal layer: yellow

bottom layer: dark grey

Product Details

Sustainability / Certifications / Approvals

APPROVALS / CERTIFICATES

  • 'Polymeric geosynthetic barrier for use in tunnels and underground structures. Fluid barrier.' according to EN 13491, certified by notified factory production control certification body 1213, certificate of conformity of the factory production control 1213-CPR-028, and provided with the CE marking.
  • 'Flexible sheets for waterproofing - Plastic and rubber damp proof sheets including plastic and rubber basement tanking sheet' according to EN 13967, certified by notified factory production control certification body 1213, certificate of conformity of the factory production control 1213-CPD-029, and provided with the CE marking.
  • Environmental safety certificate BBodSchV / M Geok E
 

Product Information

Shelf life

5 years shelf life from date of production if stored properly in undamaged, unopened, original sealed packaging

Storage conditions

Rolls must be stored in their original packaging, in a horizontal position and in cool and dry conditions. They must be protected from direct sunlight, rain, snow and ice, etc.
Do not stack pallets of rolls during transport or storage.

Effective thickness

3.00 (-5 / +10 %) mm incl. signal layer

(EN 1849–2)

Mass per area

3.81 (-5 / +10 %) kg/m2

(EN 1849–2)
System information

System structure

Ancillary Products:

  • Sikaplan® WP Disc
  • Sikaplan® W Felt PP
  • Sikaplan® W Tundrain
  • Sikaplan® WP Protection Sheet
  • Sika Waterbar® WP for forming compartments, waterproofing of concrete joints and fixations
  • Sikaplan® WP Tape
Technical Information

Resistance to impact

Watertight at 1250 mm drop height

(EN 12691)

(500 g falling weight, Method A)

Long term compression strength

Watertight at 7.0 N/mm2 (50 h)

(similar to SIA V280/14)

Tensile strength

17.0 (± 2.0) N/mm2 (machine direction)(ISO 527)
16.0 (± 2.0) N/mm2  (cross direction)

Burst strength

≥ 80 % (D=1.0 m)

(EN 14151)

Service temperature

- 10 °C min. /+ 35 °C max.

Ambient maximum temperature of liquids

+ 35 °C

Foldability at low temperature

No cracks at -20 °C

(EN 495–5)

Chemical resistance

Saturated Limewash (Test Liquid 2)

Reduction of tensile strength and elongation≤  20 %

  

5–6 % Sulfurous acid (Test Liquid 3)

Reduction of tensile strength and elongation

≤ 20 % 

Foldability at low temperatures

No cracks at -20°C

Behaviour after storage in warm water

Change of tensile strength

< 20 % (machine/ cross)

Change in elongation

< 20 % (machine/ cross)

Change of mass

< 4 %

  

Change of mass

< 10%

Resistance to oxidation

Change in elongation

≤ 10 %

Change of tensile strength

≤ 10 %

Microbiological resistance

Change in elongation

≤ 15 %

Change of tensile strength

≤ 15 %

Dimensional change after heat

< 2.0 % (machine/ cross)

(EN 1107–2)

(+80 °C / 6 h)

Reaction to fire

Class E

(EN ISO 11925-2)(EN13501-1)

Application

Application Information

Ambient air temperature

+5 °C min.
Application steps

SUBSTRATE QUALITY

In-situ concrete: Clean, sound and dry, homogeneous, free from oils and grease, dust and loose or friable particles.
Shotcrete: The profile of the shotcrete surface must not exceed a ratio of length to depth of 10:1 and its min. radius must be 20 cm. The shotcrete surface must not contain broken aggregates. Any leaks shall be sealed with Sika® waterproof plugging mortar, or drained with a Sika® FlexoDrain system. Where necessary to achieve the desired profile/surface, apply a fine sprayed concrete layer on the shotcrete surface with a min. thickness of 3-5 cm and aggregate diameter not exceeding 8 mm. Steel (girders, reinforcement mesh, anchors, etc.) must also be covered with a minimum of 4 cm fine sprayed concrete. The shotcrete surface must be clean (no loose stones, nails, wires, etc.).
A polypropylene geotextile (≥ 500 g/m2) or a compatible drainage layer must also be installed prior to the Sikaplan® WP 1100-30 HL membrane installation.