Sikaflex®-118 Extreme Grab
Construction Adhesive
Sikaflex®-118 Extreme Grab is a 1- part construction adhesive with very high initial grab which bonds most construction material substrates. Internal and external use.
- Very high initial grab
- Fixing of heavy objects without temporary fixation
- Good workability
- Very low emissions
- Adhesive-sealant with CE marking
Usage
An adhesive to bond most construction components and materials such as:- Concrete
- Masonry
- Most stones
- Ceramic
- Wood
- Metals
- Glass
- Mirrors*
Advantages
- Very high initial grab
- Fixing of heavy objects without temporary fixation
- Good workability
- Very low emissions
- Adhesive-sealant with CE marking
Packaging
290 ml cartridge, 12 cartridges per box
Colour
White, concrete grey, black
Product Details
SUSTAINABILITY
-
Conformity with LEED v4 EQc 2: Low-Emitting Materials
-
VOC emission classification GEV-EMICODE EC 1PLUS
- VOC emission classification of building materials RTS M1
- Class A+ according to French Regulation on VOC emissions
APPROVALS / CERTIFICATES
- CE Marking and Declaration of Performance to EN 15651-1 - Sealants for non-structural use in joints in buildings - Facade elements: Class F EXT-INT CC 20HM
Composition
Silane terminated polymer
Shelf life
12 months from the date of production
Storage conditions
The product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +25 °C. Always refer to packaging.
Density
~1.40 kg/l | (ISO 1183-1) |
Shore A hardness
~50 (after 28 d) | (ISO 868) |
Tensile strength
~2.2 N/mm2 | (ISO 37) |
Tear propagation resistance
~10.0 N/mm | (ISO 34) |
Service temperature
−40 °C min. / +80 °C max.
Application
Sag flow
0 mm (20 mm profile, 23 °C) | (ISO 7390) |
Ambient air temperature
+5 °C min. / +40 °C max.
Substrate temperature
+5 °C min. / +40 °C max., min. 3 °C above dew point temperature
Curing rate
~3 mm/24 h (23 °C / 50 % r.h.) | Sika Corporate Quality Procedure (CQP 049-2) |
Skinning time
~15 min (23 °C / 50 % r.h.) | (CQP 019-1) |
Yield
Yield 1 Cartridge (290 ml) | Dimension |
~100 spots | Diameter = 30 mm Thickness = 4 mm |
~5 m bead * | Nozzle diameter = 5 mm (~60 ml per linear meter) |
* Note: For heavy objects more or thicker beads (up to ~120 ml per linear metre) maybe required.
APPLICATION INSTRUCTIONS
SUBSTRATE PREPARATION
The substrate must be sound, clean, dry and free of all contaminants such as dirt, oil, grease, cement laitance, old sealants and poorly bonded paint coatings which could affect adhesion of the adhesive.
For optimum adhesion and critical, high performance applications the following priming and/or pre-treatment procedures shall be followed:
Non-porous substrates
Aluminium, anodised aluminium, stainless steel, galvanised steel, powder coated metals or glazed tiles, slightly roughen surface with a fine abrasive pad. Clean and pre-treat using Sika® Aktivator-205 applied with a clean cloth.
Before bonding / sealing, allow a waiting time of > 15 minutes (< 6 hours).
Other metals, such as copper, brass and titanium-zinc, clean and pre-treat using Sika® Aktivator-205 applied with a clean cloth. After a waiting time of > 15 minutes (< 6 hours). Apply Sika® Primer-3 N applied by brush. Allow a further waiting time of > 30 minutes (< 8 hours) before bonding / sealing.
PVC has to be cleaned and pre-treated using Sika® Primer-215 applied with a brush. Allow a waiting time of > 15 minutes (< 8 hours) before bonding / sealing.
Porous substrates
Concrete, aerated concrete and cement based renders, mortars and bricks, prime surface using Sika® Primer-3 N applied by brush.
Before bonding / sealing, allow a waiting time of > 30 minutes (< 8 hours).
For more detailed advice and instructions contact Sika Technical Services.
Note: Primers are adhesion promoters and not an alternative to improve poor preparation / cleaning of joint surfaces. Primers also improve the long term adhesion performance of a sealed joint.
CLEANING OF EQUIPMENT
Clean all tools and application equipment immediately after use with Sika® Remover-208. Once cured, hardened material can only be removed mechanically.
For cleaning skin use Sika® Hand Wipes.