Product Data Sheet Show all documents
Sikadur®-52 Normal

Sikadur®-52 Normal

Low viscosity epoxy resin

Sikadur®-52 Normal is a low viscosity, free flowing and fast curing injection resin and primer/coating based on a 2 component solvent free epoxy resin; ideally suited to a wide range of building and civil engineering applications where highly penetrative material is required. 

  • Shrink free
  • Insensitive to moisture during application, cure or whilst in service
  • Applicable over wide temperature range
  • Low viscosity
  • Excellent adhesion to most building materials even when damp
  • Proven in service
  • High tensile and flexural strength
  • Supplied in factory proportioned units
  • High early strength
  • Chemical resistant
Product Data Sheet Show all documents

Usage

Sikadur®-52 Normal may be used to inject and fill cracks between 0.2 - 5 mm wide in a wide variety of constructions applications. Sikadur®-52 Normal does not shrink on curing and forms a rigid, high strength product which exhibits excellent adhesion to most construction materials enabling the restoration of structural adequacy to columns, beams, foundations, decks and water retaining structures. Due to its highly penetrative nature Sikadur®-52 Normal is ideally suited for application as a primer beneath Sikadur epoxy mortars or Sikafloor mortars and coatings on dense substrates. Sikadur®-52 Normal may also be used to stabilise weak and friable substrates. Special high strength grades can be made to order.  

Advantages

  • Shrink free
  • Insensitive to moisture during application, cure or whilst in service
  • Applicable over wide temperature range
  • Low viscosity
  • Excellent adhesion to most building materials even when damp
  • Proven in service
  • High tensile and flexural strength
  • Supplied in factory proportioned units
  • High early strength
  • Chemical resistant

Packaging

450 ml twin cartridge
3.0 kg and 8.0 kg net pre-proportioned kits

Colour

Part A: Semi-Transparent (pale yellow),

Part B: Transparent (pale brown)

Part A+B mixed: Pale straw colouration

Product Details

Sustainability / Certifications / Approvals

APPROVALS / CERTIFICATES

ASTM C881-78 complies with Type 1, Grade 1 Class B & C
Product Information

Composition

Epoxy resin

Shelf life

Minimum shelf life is approximately 3 years 

Storage conditions

Store in original, unopened, sealed and undamaged packaging in dry conditions at temperatures between +5 °C and +30 °C. 

Density

1.1 kg/litre (component A+B mixed) (at +23 °C)
 

Viscosity

Temperature

Viscosity

+20 °C

~300 mPa.s 

+35 °C

~110 mPa.s

Note: 1 mPa.s = 1 centipoise (cps)
Technical Information

Compressive strength

+20 oC

1 day

~44 MPa

7 days

~54 MPa

Tensile strength

~22 MPa (after 7 days at +20 oC)

(BS 6319)

Tensile adhesion strength

+20 oC

Adhesion to concrete

>3.5 MPa

Adhesion to sandblasted steel

~10 MPa

Application

Application Information

Mixing ratio

A : B = 2 : 1 by weight and volume

Ambient air temperature

+5 oC to +30 oC

Substrate temperature

+5 oC to +30 oC

Pot Life

Temperature

Time

5oC

~ 70 minutes

20oC

~ 27 minutes

35oC~ 16 minutes
Consumption

Consumption

1.1 kg/m2 approx. per mm thickness
(dependent on surface profile, texture, temperature, porosity and wastage)
Application steps

SUBSTRATE PREPARATION

All surfaces to be coated, should be mechanically roughened, free from all contaminants (eg. dust, oil, grease, etc.) surface water, laitance, old coatings, corrosion products. Suitable methods of preparation include blast cleaning and scabbling. For optimum penetration the substrate should be dry.
When Sikadur®-52 Normal is used to inject cracks, the cracks must be blown out with oil free, dry compressed air. Cracks in the width range of 0.2 - 5 mm may be successfully injected.

MIXING

Sikadur®-52 Normal is supplied in factory proportioned units comprising the correct quantities of Part A (Resin) and Part B (Hardener). Thoroughly stir both components separately using a slow running drill with a windmill type paddle (max. speed 600 rpm). Decant all of Part B into Part A and mix thoroughly (typically 3 mins). (Not applicable to twin cartridge packs).

CLEANING OF EQUIPMENT

Uncured material may be cleaned from application tools, etc. by using Sika Colma Cleaner (flammable solvent). Cured material can only be removed mechanically.